Biodegradable magnesium alloy implant

ABSTRACT

A biodegradable implant is formed of a magnesium alloy having 3 to 7% by weight Zn, 0.001 to 0.5% by weight Ca, the remainder being magnesium containing total impurities, which promote electrochemical potential differences and/or the formation of intermetallic phases, in a total amount of no more than 0.0048% by weight, wherein the total impurity contains elements selected from a first group of Fe, Si, Mn, Co, Ni, Cu, Al, Zr and P and elements selected from a second group of rare earths having the ordinal numbers 21, 39, 57 to 71 and 89 to 103.

PRIORITY CLAIM

This application claims priority under 35 U.S.C. § 120 and is a continuation of U.S. application Ser. No. 14/395,713, filed on Oct. 20, 2014, which application was a U.S. National Phase under 35 U.S.C. § 371 of International Application No. PCT/EP2013/063111, filed Jun. 24, 2013, and which claims priority to U.S. Provisional Application No. 61/664,274, filed Jun. 26, 2012.

FIELD OF THE INVENTION

A field of the invention relates to magnesium alloy implants. Implants include cardiovascular, osteosynthesis, and tissue implants. Particular applications include stents, valves, closure devices, occluders, clips, coils, staples, implantable regional drug delivery devices, implantable electrostimulators (like pacemakers and defibrillators), implantable monitoring devices, implantable electrodes, systems for fastening and temporarily fixing tissue implants and tissue transplantations. Additional example applications include implantable plates, pins, rods, wires, screws, clips, nails, and staples.

BACKGROUND

Magnesium properties are defined by the type and quantity of the alloying elements and impurities as well as the production conditions. Some effects of the alloying elements and impurities on the properties of the magnesium alloys have been long known to artisans. However, the properties of binary or ternary magnesium alloys for the use thereof as implant materials remains complex to determine.

The alloying element used most frequently for magnesium is aluminum, resulting in increased tensile strength due to solid solution and precipitation hardening and fine grain formation, but also in microporosity. Moreover, in the melt aluminum shifts the iron precipitation boundary toward drastically lower iron contents at which the iron particles precipitate or form intermetallic particles together with other elements.

Calcium exhibits a pronounced grain refining effect and worsens the castability and corrosion resistance.

Undesirable accompanying elements in magnesium alloys include iron, nickel, cobalt and copper, which cause a considerable increase in the corrosion tendency due to the electropositive nature thereof.

Manganese can be found in all magnesium casting alloys and binds iron in the form of AlMnFe precipitations, whereby the formation of local elements is reduced. On the other hand, manganese is not able to bind all the iron, and therefore a remainder of iron and a remainder of manganese always remain in the melt.

Silicon lowers the castability and viscosity, and as the content of Si rises, a worsened corrosion behavior is to be expected. Iron, manganese and silicon have a very high tendency to form an intermetallic phase. The electrochemical potential of this phase is very high and can thus act as a cathode controlling the corrosion of the alloy matrix.

As a result of solid solution hardening, zinc improves the mechanical properties and results in grain refining, however it also leads to microporosity with a tendency toward hot cracking starting at a content of 1.5 to 2% by weight in binary Mg—Zn and ternary Mg—Al—Zn alloys.

Alloying additions made of zirconium increase the tensile strength without lowering the expansion and lead to grain refining, but also to a strong impairment of dynamic recrystallization, which is manifested in an increase of the recrystallization temperature and therefore requires high energy expenditure. Moreover, zirconium cannot be added to melts containing aluminum and silicon because the grain refining effect is lost.

Rare earths such as Lu, Er, Ho, Th, Sc and In all exhibit a similar chemical behavior and form eutectic systems with partial solubility on the magnesium-rich side of the binary phase diagrams such that precipitation hardening is possible.

The addition of further alloying elements, in conjunction with the impurities, is known to cause the formation of different intermetallic phases in binary magnesium alloys. For example, the intermetallic phase Mg₁₇Al₁₂ forming at the grain boundaries is brittle and limits the ductility. As compared to the magnesium matrix, this intermetallic phase is more noble and able to form local elements, whereby the corrosion behavior worsens.

In addition to these influencing factors, the properties of the magnesium alloys also depend on the metallurgical production conditions. Conventional casting methods automatically introduce impurities when adding, by alloying, the alloying elements. The prior art (U.S. Pat. No. 5,055,254 A) defines tolerance limits for impurities in magnesium casting is alloys, which, for example for a magnesium-aluminum-zinc alloy containing approximately 8 to 9.5% Al and 0.45 to 0.9% Zn, mentions tolerance limits of 0.0015 to 0.0024% Fe, 0.0010% Ni, 0.0010 to 0.0024% Cu and no less than 0.15 to 0.5% Mn.

Tolerance limits for impurities in magnesium and the alloys therefore are stated in a variety of technical literature as follows:

Alloy Production State Fe Fe/Mn Ni Cu Pure Mg no information 0.017 0.005 0.01 AZ 91 Die casting F 0.032 0.005 0.040 High-pressure 0.032 0.005 0.040 die casting Low-pressure 0.032 0.001 0.040 die casting T4 0.035 0.001 0.010 T6 0.046 0.001 0.040 Gravity die F 0.032 0.001 0.040 casting AM60 Die casting F 0.021 0.003 0.010 AM50 Die casting F 0.015 0.003 0.010 AS41 Die casting F 0.010 0.004 0.020 AE42 Die casting F 0.020 0.020 0.100

It has been found that these tolerance definitions are not sufficient to reliably exclude the formation of corrosion-promoting intermetallic phases, which in terms of electrochemistry have a more noble potential than the magnesium matrix.

Biodegradable implants require a load-bearing function and consequently strength, together with sufficient expandability, during the physiologically necessary support periods thereof. However, especially in this respect, the known magnesium materials fall far short of the strength properties provided by permanent implants such as titanium, CoCr alloys and titanium alloys. The ultimate tensile strength R_(m) for implants is approximately 500 MPa to >1000 MPa, while that of magnesium materials is <275 MPa so far, and in most cases <250 MPa.

Another drawback of many technical magnesium materials is that the difference thereof between ultimate tensile strength R_(m) and proof stress R_(p) is small. In the case of implants that allow plastic deformation, such as cardiovascular stents, this means that no further resistance exists against deformation after initial deformation of the material, and the regions that have already been deformed are deformed further without any load increase This can lead to overstretching of parts of the component and fracture may occur.

Many magnesium materials, such as the alloys of the AZ group, for example, additionally exhibit a clearly pronounced mechanical asymmetry, which is manifested in the difference in the mechanical properties, especially the proof stress R_(p) with tension load and compression load. Such asymmetries are created, for example, during forming processes such as extrusion, rolling and drawing, which are used to produce suitable semi-finished products. A difference between the proof stress R_(p) during tension and the proof stress R_(p) during compression that is too large may result in inhomogeneous deformation of a component, such as a cardiovascular stent, which later undergoes multiaxial deformation, and may cause cracking and fracture.

Because of the low number of crystallographic slip systems, magnesium alloys can generally also form textures during forming processes such as extrusion, rolling and drawing used to produce suitable semifinished products by orienting the grains during the forming process. Specifically, the semifinished product has different properties in different directions in space. For example, high deformability or elongation at fracture occurs in one direction in space after forming, and reduced deformability or elongation at fracture occurs in another direction in space. The formation of such textures should likewise be avoided, because a stent is subjected to high plastic deformation, and reduced elongation at fracture increases the risk of failure of the implant. One method for substantially avoiding such textures during forming is to adjust as fine a grain as possible prior to forming. Because of the hexagonal lattice structure of magnesium materials, the ability of these materials to deform at room temperature is low, which is characterized by slip in the base plane. If the material additionally has a coarse microstructure, i.e., a coarse grain, so-called twinning is forcibly produced upon further deformation, at which shear strain occurs, which transforms a crystal region into a position that is mirror symmetrical to the starting position.

The resulting twin grain boundaries constitute weak points in the material, where incipient cracking starts, especially with plastic deformation, which ultimately leads to the destruction of the component.

If the grain of the implant materials is sufficiently fine, the risk of such implant failure is drastically reduced. Implant materials should therefore have as fine a grain as possible so as to prevent such undesirable shear strain.

All available magnesium materials for implants are subject to high corrosion in physiological media. Attempts have been made in the prior art to curb the corrosion tendency by providing the implants with a corrosion-inhibiting coating, for example made of polymeric materials (EP 2 085 100 A2, EP 2 384 725 A1), an aqueous or alcoholic conversion solution (DE 10 2006 060 501 A1) or an oxide (DE 10 2010 027 532 A1, EP 0 295 397 A1).

The use of polymeric passivation layers is controversial, because virtually all appropriate polymers also cause strong inflammations in the tissue at times. Thin structures without such protective measures do not provide the required support periods. The corrosion on thin-walled traumatological implants is often times accompanied by an excessively fast loss of tensile strength, which poses an additional burden by forming excessive amounts of hydrogen per unit of time. The consequences are undesirable gas inclusions in the bones and tissue.

In the case of traumatological implants having larger cross-sections, there is a need to be able to deliberately control the hydrogen problem and the corrosion rate of the implant by way of the structure thereof.

Specifically with biodegradable implants, there is a desire for maximum biocompatibility of the elements, because all the chemical elements that are contained are absorbed by the body after decomposition. In any case, highly toxic elements such as Be, Cd, Pb, Cr and the like should be avoided.

Degradable magnesium alloys are especially suitable for implementing implants which have been employed in a wide variety of forms in modern medical technology. Implants are used, for example, to support vessels, hollow organs and vein systems (endovascular implants, such as stents), for fastening and temporarily fixing tissue implants and tissue transplantations, but also for orthopedic purposes, such as nails, plates or screws. A particularly frequently used form of an implant is the stent.

The implantation of stents has become established as one of the most effective therapeutic measures for the treatment of vascular diseases. Stents have the purpose of assuming a supporting function in hollow organs of a patient. For this purpose, stents featuring conventional designs have a filigree supporting structure comprising metal struts, which is initially present in compressed form for introduction into the body and is expanded at the site of the application. One of the main application areas of such stents is to permanently or temporarily widen and hold open vascular constrictions, particularly constrictions (stenosis) of coronary blood vessels. In addition, aneurysm stents are known, which are used primarily to seal the aneurysm. The support function is additionally provided.

A stent has a base body made of an implant material. An implant material is a non-living material, which is employed for applications in medicine and interacts with biological systems. A basic prerequisite for the use of a material as an implant material, which is in contact with the body environment when used as intended, is the body friendliness thereof (biocompatibility). For the purpose of the present application, biocompatibility shall be understood to mean the ability of a material to induce an appropriate tissue reaction in a specific application. This includes an adaptation of the chemical, physical, biological, and morphological surface properties of an implant to the recipient's tissue with the aim of a clinically desired interaction. The biocompatibility of the implant material is also dependent on the temporal process of the reaction of the biosystem in which it is implanted. For example, irritations and inflammations occur in a relatively short time, which can lead to tissue changes. Depending on the properties of the implant material, biological systems thus react in different ways. According to the reaction of the biosystem, the implant materials can be divided into bioactive, bioinert and degradable or resorbable materials.

Conventional implant materials include polymers, metallic materials, and ceramic materials (as coatings, for example). Biocompatible metals and metal alloys for permanent implants include, for example, stainless steels (such as 316L), cobalt-based alloys (such as CoCrMo cast alloys, CoCrMo forge alloys, CoCrWNi forge alloys and CoCrNiMo forge alloys), pure titanium and titanium alloys (such as cp titanium, TiAl6V4 or TiAl6Nb7) and gold alloys. In the field of biocorrodible stents, the use of magnesium or pure iron as well as biocorrodible base alloys of the elements magnesium, iron, zinc, molybdenum, and tungsten are known.

The use of biocorrodible magnesium alloys for temporary implants having filigree structures is made difficult in particular in that the degradation of the implant progresses very quickly in vivo. Alloy composition and coatings are approaches to slow the degradation of the implant material While the existing approaches have shown promise, none of them has so far led to a commercially available product to the knowledge of the inventors. Regardless of the efforts made so far, there remains a continuing need for solutions that make it possible to at least temporarily reduce the corrosion of magnesium alloys in vivo, while optimizing the mechanical properties thereof at the same time.

SUMMARY OF THE INVENTION

Preferred embodiments of the invention provide a biodegradable magnesium alloy implant, and a method for the production thereof. The magnesium matrix of the implant can remain in an electrochemically stable state over the required support period with fine grain and high corrosion resistance without protective layers, leverages the formation of intermetallic phases, which electrochemically are more noble than the magnesium matrix, while also improving the mechanical properties, such as increasing the tensile strength and proof stress, as well as reducing the mechanical asymmetry so as to adjust the degradation rate of the implants.

A preferred biodegradable implant is formed of a magnesium alloy having 3 to 7% by weight Zn, 0.001 to 0.5% by weight Ca, the remainder being magnesium containing total impurities, which promote electrochemical potential differences and/or the formation of intermetallic phases, in a total amount of no more than 0.0048% by weight, wherein the total impurity contains elements selected from a first group of Fe, Si, Mn, Co, Ni, Cu, Al, Zr and P and elements selected from a second group of rare earths having the ordinal numbers 21, 39, 57 to 71 and 89 to 103t.

A preferred method for producing a magnesium alloy having improved mechanical and electrochemical properties includes generating a high-purity magnesium by vacuum distillation. A billet of the alloy is generated by synthesis of the high-purity magnesium according with high-purity Zn and Ca in a composition of 3 to 7% by weight Zn, 0.001 to 0.5% by weight Ca, the remainder being magnesium containing total impurities, which promote electrochemical potential differences and/or the formation of intermetallic phases, in an amount of no more than 0.0048 by weight wherein the total impurity contains individual impurities selected from the group of Fe, Si, Mn, Co, Ni, Cu, Al, Zr and P in an amount of not more than 0.0038% of weight; with the alloying elements are selected from the group of the rare earths having the ordinal numbers 21, 39, 57 to 71 and 89 to 103 in a total amount of no more than 0.001% by weight. The alloy is homogenized by annealing at a temperature between 350° C. and 450° C. with a holding period of 4 to 40 hours. The homogenized alloy is formed in the temperature range between 250° C. and 350° C. The formed alloy is optionally heat treated in the temperature range between 100° C. and 300° C. with a holding period of 1 minute to 3 hours.

DETAILED DESCRIPTION OF THE PREFERRED EMBODIMENTS

The magnesium alloy implant according to the invention has extraordinarily high corrosion resistance, which is achieved by drastically reducing the content of individual impurities and the combinations thereof in the magnesium matrix, and by also adding precipitation and solid solution hardenable elements, which are present in completely solid solution. The microstructure that is obtained has no electrochemical potential differences between the individual matrix phases after the forming and heat treatment processes, and therefore these differences cannot expedite the corrosion in physiological media. The solution according to the invention is based on the realization that the corrosion resistance and deformability of the magnesium matrix of the implant must be assured over the support period such that the implant is able to absorb multiaxial permanent load without fracture or cracking, and to also utilize the magnesium matrix as a means for the decomposition triggered by the physiological liquids.

The applicant surprisingly found that the alloy matrix, having a content of 3 to 5% by weight Zn and 0.2 to 0.4% by weight Ca, has a more noble electrochemical potential than the intermetallic phase Ca₂Mg₆Zn₃, while the MgZn phase, which can be precipitated by heat treatment, is considerably more noble as compared to the alloy matrix, whereby the MgZn phase can be precipitated from the lattice of the alloy matrix by means of targeted heat treatment and can act as cathodes for the alloy matrix. This provides the option of deliberately influencing the degradation rate of the alloy matrix.

Another surprising result is that, despite freedom of Zr, or Zr contents that are considerably lower than those stated in the prior art, a grain refining effect can be achieved which is attributed to the intermetallic phase Ca₂Mg₆Zn₃, which blocks the movements of the grain boundaries, limits the grain size during recrystallization and thus prevents undesirable grain growth, while also increasing the proof stress and tensile strength values.

Within the aforementioned mechanical properties, a Zr content of <0.0003% by weight, and preferably <0.0001% by weight, is advantageous for the magnesium alloy according to the invention.

The previously known tolerance limits for the individual impurities within the total impuritiy do not take into account that wrought magnesium alloys often times are subjected to a thermomechanical treatment, and more particularly to an extended annealing process, which creates the near-equilibrium structures. The metallic elements bond by way of diffusion and form what are known as intermetallic phases, which have a different electrochemical potential, notably a considerably higher potential, than the magnesium matrix, and therefore these intermetallic phases act as cathodes and can trigger galvanic corrosion processes.

The applicant found that a formation of such intermetallic phases can be reliably prevent when complying with the following tolerance limits of the individual impurities within the total impurity:

Fe, Si, Mn, Co, Ni, Cu each with <0.0005% by weight; Zr, Al each with <0.0003% by weight; and P<0.0002% by weight.

It is noted that in this embodiment the total impurity additionally contains individual impurities selected from the group of rare earths having the ordinal numbers 21, 57 to 71 and 89 to 103 in total <0.001% by weight, preferably no more than 0.0005% by weight and still more preferably no more than 0.0003% by weight.

Preferably, the corrosion-staple alloy matrix contains total impurities in a total amount of no more than 0.0036% by weight, containing individual impurities selected from the group of Fe, Si, Mn, Co, Ni, Al, Zr, and P of in total no more than 0.0026% by weight, wherein the total amount can be achieved when complying with the following tolerance limits of individual impurities in % by weight:

Fe, Si, Mn each with <0.0005; Co, Ni, Cu each with <0.0002; Zr, <0.0003; and P, Al each with <0.0001.

Additionally the total impurities contain the preferred amount of rare earths having the ordinal numbers 21, 57 to 71 and 89 to 103 in total <0.001.

In particular preferred the corrosion-staple alloy matrix contains total impurities in a total amount of no more than 0.00215% by weight, containing individual impurities selected from the group of Fe, Si, Mn, Co, Ni, Al, Zr, and P of in total no more than 0.00115% by weight, wherein the total amount can be achieved when complying with the following tolerance limits of individual impurities in % by weight:

Fe, Si, Mn each with <0.0002; Co, Ni, Cu, Zr, P each with <0.0001; and Al <0.00005.

Additionally the total impurities contain the preferred amount of rare earths having the ordinal numbers 21, 57 to 71 and 89 to 103 in total <0.001.

When the individual impurities are combined, the formation of intermetallic phases, which are more noble than the alloy matrix, is suppressed if the sum of individual impurities consisting of Fe, Si, Mn, Co, Ni, Cu and Al is no more than 0.0033% by weight, preferably no more than 0.0022% by weight, still more preferably no more than 0.00095% by weight, the content of Al is no more than 0.0003% by weight, preferably no more than 0.0001% by weight, particularly preferably no more than 0.00005% by weight and the content of Zr is preferably no more than 0.0003% by weight, preferably no more than 0.0001% by weight.

There are different mechanisms of action by which the aforementioned individual impurities impair the corrosion resistance of the material.

If small Fe particles form in the alloy because of a high Fe content, these particles will act as cathodes for a corrosive attack; the same applies to Ni and Cu.

Moreover, especially Fe and Ni with Zr, but also Fe, Ni and Cu with Zr, can precipitate as intermetallic particles in the melt; these will also act as very effective cathodes for corrosion of the matrix.

Intermetallic particles having a very high potential difference as compared to the matrix and a very high formation tendency include the phases of Fe and Si and Fe, Mn and Si, which is why contaminations containing these elements must be minimized.

The content of P should be minimized to the extent possible, because Mg phosphides form even when minute amounts of P are present and dramatically impair the mechanical properties of the structure.

Such low concentrations thus ensure that the magnesium matrix no longer contains any intermetallic phases, which have a more positive electrochemical potential as compared to the matrix.

In the preferred magnesium alloy according to the invention, the sum of the contents of elements of the rare earths and scandium (ordinal numbers 21, 57 to 71 and 89 to 103) is less than 0.001% by weight, preferably less than 0.0005% by weight and still more preferably less than 0.0003.

These additions make it possible to increase the tensile strength of the magnesium matrix and raise the electrochemical potential of the matrix, whereby a corrosion-reducing action, notably with respect to physiological media, develops. The precipitations preferably have a size of no more than 5 μm, and preferably of no more than 1 μm, and are located on the grain boundaries and in the grain interior, whereby the movement of grain boundaries during thermal treatment as well as dislocations during deformation are impaired and the strength of the magnesium alloy is increased.

The magnesium alloy according to the invention achieves a tensile strength of >275 MPa, and preferably >300 MPa, a yield point of >200 MPa, and preferably >225 MPa, and a yield ratio of <0.8, and preferably <075, wherein the difference between the tensile strength and yield point is >50 MPa, and preferably >100 MPa, and the mechanical asymmetry is <1.25.

These significantly improved mechanical properties of the novel magnesium alloys assure that the implants, for example cardiovascular stents, are able to withstand the multiaxial permanent load in the implanted state over the entire support period, despite onsetting degradation of the magnesium matrix due to corrosion.

So as to minimize the mechanical asymmetry, it is preferable for the magnesium alloy to have a particularly fine microstructure having a grain size of no more than 5 μm.

A preferred method for producing a magnesium alloy having improved mechanical and electrochemical properties is provided. The method includes the following steps:

-   a) generating a high-purity magnesium by way of vacuum distillation; -   b) generating a billet of the alloy by synthesis of the magnesium     according to step a) with high-purity Zn and Ca in a composition of     3 to 7% by weight Zn, 0.001 to 0.5% by weight Ca, the remainder     being magnesium containing total impurities, which promote     electrochemical potential differences and/or the formation of     intermetallic phases, in a amount of no more than 0.0048 by weight,     preferably no more than 0.0045% by weight and still more preferably     no more than 0.0036% by weight, wherein the total impurity contains     individual impurities selected from the group of Fe, Si, Mn, Co, Ni,     Cu, Al, Zr and P in an amount of not more than 0.0038% of weight;     and wherein the alloying elements are selected from the group of the     rare earths having the ordinal numbers 21, 39, 57 to 71 and 89 to     103 in a total amount of no more than 0.001% by weight; -   c) homogenizing the alloy by annealing at a temperature between     350° C. and 450° C. with a holding period of 4 to 40 hours; -   c) at least single forming of the homogenized alloy in the     temperature range between 250° C. and 350° C.; and -   d) optionally heat treating the formed alloy in the temperature     range between 100° C. and 300° C. with a holding period of 1 minute     to 3 hours.

A content of preferably 3 to 5% by weight Zn and a content of 0.2 to 0.4% by weight Ca assure that volume contents of up to 2% of the intermetallic phase and the precipitable MgZn phase, respectively, are created in the matrix lattice. The electrochemical potentials of the two phases differ considerably, the MgZn phase being more noble than the matrix and the Ca₂Mg₆Zn₃ phase being less noble than the matrix. By means of the heat treatment, the MgZn phase can be prompted to precipitate to the desired degree in a regime preselected by the temperature and holding period, whereby the degradation rate of the alloy matrix can be adjusted.

In addition to the corrosion-inhibiting action, the intermetallic Ca₂Mg₆Zn₃ phase also has the surprising effect of grain refining created by the forming process, which results in a considerable increase in tensile strength and proof stress. This allows Zr to be dispensed with as an alloying element and the temperatures for the recrystallization to be lowered.

Vacuum distillation is preferably used to produce a starting material for a high-purity magnesium-zinc-calcium alloy having the required threshold values.

The sum of impurities and the content of addition elements triggering the precipitation and solid solution hardening and raising the matrix potential can be selectively adjusted and in % by weight are:

-   a) for the individual impurities:     -   Fe, Si, Mn, Co, Ni, Cu each with <0.0005% by weight;     -   Al, Zr each with <0.0003% by weight;     -   and P<0.0002% by weight.     -   It is noted that in this embodiment the total impurity         additionally contains individual impurities selected from the         group of rare earths having the ordinal numbers 21, 57 to 71 and         89 to 103 in total <0.001% by weight.     -   aa) for the individual impurities in a preferred amount of         impurities of no more than 0.0026% by weight:         -   Fe, Si, Mn each with <0.0005;         -   Co, Ni, Cu each with <0.0002;         -   Zr, <0.0003; and         -   Al, P each with <0.0001.         -   In this preferred embodiment the amount of total impurities             which is the sum of the individual impurities and the             impurities selected from the group of rare earths having the             ordinal numbers 21, 57 to 71 and 89 to 103 is in total             <0.0036% by weight.     -   ab) for the individual impurities in a particularly preferred         amount of impurities of no more than 0.00115% by weight:         -   Fe, Si, Mn each with <0.0002;         -   Co, Ni, Cu, Zr, P each with <0.0001; and         -   Al<0.0001.         -   In this preferred embodiment the amount of total impurities             which is the sum of the individual impurities and the             impurities selected from the group of rare earths having the             ordinal numbers 21, 57 to 71 and 89 to 103 is in total             <0.00215% by weight. -   b) for the combination of individual impurities in total:     -   Fe, Si, Mn, Co, Ni, Cu and Al no more than 0.0033% by weight,         preferably no more than 0.0022% by weight, still more preferably         0.00095% by weight, the content of Al no more than 0.0003         preferably no more than 0.0001% by weight, particularly         preferably no more than 0.00005% by weight, and the content of         Zr is no more than 0.0003% by weight, preferably no more than         0.0001% by weight; -   c) for the addition elements which are also contained in the total     impurities:     -   rare earths in a total amount of no more than 0.001% by weight,         preferably no more than 0.0005% by weight.

It is particularly advantageous that the method according to the invention only requires a small number of forming steps. Extrusion, equal channel angular extrusion and/or multiple forging can thus preferably be employed, which assure that a substantially homogeneous fine grain of <15 μm is achieved.

Because of the heat treatment, MgZn precipitations having a grain size of 1 nm to 50 nm in a fine-grained structure having a grain size of preferably <7.5 μm dispersely distributed at the grain boundaries and in the interior of the grains, whereby the tensile strength of the alloy reaches values which at >275 MPa, and preferably >300 MPa, are considerably higher than the prior art.

The invention also relates to the use of the magnesium alloy produced according to the invention, which has the above described advantageous composition and structure, in medical technology, notably for the production of implants, for example endovascular implants such as stents, for fastening and temporarily fixing tissue implants and tissue transplantations, orthopedic and dental implants, and neuroimplants.

Preferred implants in the sense of this patent application are in the Cardiovascular field, osteosynthesis field or other areas.

Cardiovascular field in the sense of this application includes

-   -   the field of diagnostic, prevention and treatment of all         diseases of the cardiovascular system, i.e. heart and blood         vessel system,     -   by mean of active and non-active implants used to support         vessels, and vein systems     -   including coronary, cerebral and peripheral vascular implants         like stents, valves, closure devices, occluders, clips, coils,         staples, implantable regional drug delivery devices,     -   implantable electrostimulators (like pacemakers and         defibrillators), implantable monitoring devices, implantable         electrodes,     -   system for fastening and temporarily fixing tissue implants and         tissue transplantations     -   field also includes any type of stent as mechanical fix or         temporary scaffold to support hollow organs including bones,         intervertebral disks

Osteosynthesis in the sense of this application includes the field of treatment of fractured bones for internal fixation and stabilization by mechanical devices such as metal plates, pins, rods, wires, screws, clips, nails, staples excluding stent technology

Examples of areas out of the osteosynthesis field or the cardiovascular field are:

-   -   Devices for the treatment of diseases of the sinews, joints,         muscles, cartilages,     -   oral (including dental) and maxillo facial implants (excl.         osteosynthesis means),     -   esthetic implants,     -   supporting tools out of the body,     -   tissue engineering,     -   soft tissue implants,     -   devices for wound care,     -   suture material and clamps,     -   neurosurgery     -   local drug delivery (excl. cardiovascular, i.e. lever)     -   renal applications

EXAMPLE

A magnesium alloy is generated which is composed of 5% by weight Zn and 0.15% by weight Ca, the remainder being Mg, and contains the following individual impurities in % by weight:

Fe: <0.0005; Si: <0.0005; Mn: <0.0005; Co: <0.0002; Ni: <0.0001; Cu<0.0002, wherein the sum of individual impurities consisting of Fe, Si, Mn, Co, Ni, Cu and Al should be no more than 0.0015% by weight, the content of Al<0.001% by weight and that of Zr <0.0003% by weight, and the content of rare earths having the ordinal numbers 21, 39, 57 to 71 and 89 to 103 in total should be less than 0.001% by weight, which leads to an alloy with total impurities of in total no more than 0.0035% by weight.

This alloy, produced using magnesium vacuum distillation, is subjected to homogenizing annealing at a temperature of 350° C. for a duration of 12 hours, and subsequently to multiple extrusion processes at a temperature of 300° C., so as to produce a precision tube for a cardiovascular stent.

The subsequent heat treatment was carried out at a temperature of 250° C. with a holding period of 0.1 hour. The grain size was <7.5 μm.

The magnesium alloy reached a tensile strength of 310 to 320 MPa and proof stress of <250 MPa [sic]. The yield ratio was 0.7 and the mechanical asymmetry was 1.2.

In artificial body fluid, the Ca₂Mg₆Zn₃ phase degraded more quickly than the matrix and is therefore less noble than the matrix. This means that these intermetallic particles cannot act as cathodes for the alloy matrix. The MgZn phase expedited the degradation in artificial body fluid and was therefore more noble electrochemically than the alloy matrix, whereby it is able to induce corrosion.

Because of the subsequent heat treatment, it is thus possible to precipitate the MgZn phase from the alloy matrix, rendering the alloy matrix less noble.

The subsequent degradation rate under physiological usage conditions can thus be adjusted by means of the heat treatment.

While specific embodiments of the present invention have been shown and described, it should be understood that other modifications, substitutions and alternatives are apparent to one of ordinary skill in the art. Such modifications, substitutions and alternatives can be made without departing from the spirit and scope of the invention, which should be determined from the appended claims.

Various features of the invention are set forth in the appended claims. 

1. A biodegradable implant comprising a magnesium alloy having 3 to 7% by weight Zn, 0.001 to 0.5% by weight Ca, the remainder being magnesium containing total impurities, which promote electrochemical potential differences and/or the formation of intermetallic phases, in a total amount of no more than 0.0048% by weight, wherein the total impurity contains elements selected from a first group of Fe, Si, Mn, Co, Ni, Cu, Al, Zr and P and elements selected from a second group of rare earths having the ordinal numbers 21, 39, 57 to 71 and 89 to
 103. 2. The biodegradable implant of claim 1, comprising a total amount of no more than 0.0038% of the first group.
 3. The biodegradable implant of claim 1, comprising a total amount of no more than 0.001% of the second group.
 4. The biodegradable implant of claim 1, wherein the content of Zn is 3 to 5% by weight and that of Ca is at least 0.2 to 0.4% by weight.
 5. The biodegradable implant of claim 1, wherein the alloy contains an intermetallic Ca₂Mg₆Zn₃ phase in a volume content of greater than 0 to 2%.
 6. The biodegradable implant of claim 1, comprising total impurities limited in % by weight: Fe<0.0005; Si<0.0005; Mn<0.0005; Co<0.0005; Ni<0.0005; Cu<0.0005; Al<0.0003; Zr<0.0003; P<0.0002.
 7. The biodegradable implant of claim 1, wherein the impurity elements Fe, Si, Mn, Co, Ni, Cu and Al total no more than 0.0033% by weight, the content of Al is no more than 0.0003% by weight, and the content of Zr is no more than 0.0001% by weight
 8. A method for producing a magnesium alloy implant having improved mechanical and electrochemical properties, comprising a) generating a high-purity magnesium by vacuum distillation; b) generating a billet of the alloy by synthesis of the high-purity magnesium with high-purity Zn and Ca in a composition of 3 to 7% by weight Zn, 0.001 to 0.5% by weight Ca, the remainder being magnesium containing total impurities, which promote electrochemical potential differences and/or the formation of intermetallic phases, in a total amount of no more than 0.0048% by weight, wherein the total impurity contains elements selected from a first group of Fe, Si, Mn, Co, Ni, Cu, Al, Zr and P and elements selected from a second group of rare earths having the ordinal numbers 21, 39, 57 to 71 and 89 to 103; c) homogenizing the alloy by annealing at a temperature between 350° C. and 450° C. with a holding period of 4 to 40 hours; and d) forming of the homogenized alloy in the temperature range between 250° C. and 350° C.
 9. The method according to claim 8, further comprising heat treating the homogenized alloy in the temperature range between 100° C. and 300° C. with a holding period of 1 minute to 3 hours. 